Minimum Order Quantity | 10 Kilogram |
Size | 10-100mm |
Grade | C18150,C18200 |
Chromium | 1% |
Color | Copper |
Surface Finishing | Bright |
Finish | Bright |
I Deal In | New Only |
Brand | iBeCu |
Material Type | Copper Chromium Zirconium Alloy |
Shape | Round Bar,Flats,Wires |
Usage/Application | Welding |
Alloy | CuCrZr C18150 |
Cu Content | 99 |
Density | 8,3 |
Diameter | All |
C18150 Copper Chromium Zirconium Alloys
RWMA Class:Class 2
Principal Element:Cu,Cr,Zr
Shape:Round Bar,Flat Bar,Square Bar,Plate,Wheel.
C18150 Chromium Zirconium Copper. CuCr1Zr – UNS.C18150 Chromium Zirconium Copper C18150 is an excellent and unique copper alloy with high electrical conductivity, hardness, and ductility, moderate strength, and excellent resistance to softening at elevated temperatures. The addition of 0.1% zirconium (Zr) and 1.0% chromium (Cr) to copper results in a heat treatable alloy which may be solution treated and subsequently aged to produce these desirable properties. Rod is usually supplied from the mill in the fully aged and drawn condition so no further heat treatment is required by the fabricator. The softening temperature of properly heat treated C18150 rod exceeds 500°C as compared to unalloyed pure copper which softens at 200°C, and silver bearing coppers which soften at 350°C.Minimum Order Quantity | 10 Kg |
Grade | C18200 |
Size/Diameter | >4 inch |
Brand | IBECU |
Diameter | 8 TO 200 |
Shape | ROUND,SQUARE |
I Deal In | New Only |
Material | Chromium Coppe |
C18150 Copper Chromium Zirconium Alloys
RWMA Class:Class 2
Principal Element:Cu,Cr,Zr
Shape:Round Bar,Flat Bar,Square Bar,Plate,Wheel.
Minimum Order Quantity | 10 Kilogram |
Size | 10-50mm |
Chromium | 1% |
Color | Copper |
Finish | Copper |
I Deal In | New Only |
Brand | IBeCu |
Form | round,square,flat |
Length | 2 mtrs |
Grade | C18200,C18150 |
Diameter | 10-100 |
Usage/Application | Welding |
C18150 Chromium Zirconium Copper
CuCr1Zr – UNS.C18150 Chromium Zirconium Copper C18150 is an excellent and unique copper alloy with high electrical conductivity, hardness, and ductility, moderate strength, and excellent resistance to softening at elevated temperatures. The addition of 0.1% zirconium (Zr) and 1.0% chromium (Cr) to copper results in a heat treatable alloy which may be solution treated and subsequently aged to produce these desirable properties. Rod is usually supplied from the mill in the fully aged and drawn condition so no further heat treatment is required by the fabricator. The softening temperature of properly heat treated C18150 rod exceeds 500°C as compared to unalloyed pure copper which softens at 200°C, and silver bearing coppers which soften at 350°C.Minimum Order Quantity | 500 Piece |
Application | Series welding backing dies. |
Allloy | C18150 CuCrZr,EN ISO 5182 A2/2 |
Chemical | Cr 0.7% to 1.2%,Zr 0.06% to 0.15%. |
Grade | CuCrZr. C18150 |
Density | 8.9g/cm3 |